Complex shapes can be molded at low cost and in a short time using silicone molds. Excellent strength, heat resistance, and workability. *Demonstrations and samples available.
The nylon 6 monomer raw material "3NI-NYLON" consists of two components: a "main agent and a curing agent," with the polymerization speed adjusted. They are each sealed in metal cans, allowing for heating and melting in the can, enabling immediate molding. The containers have excellent gas barrier properties and heat resistance, making long-term storage possible. 【Characteristics of "3NI-NYLON" in terms of physical properties】 ■ Can be used as an alternative to metal materials ■ Excellent mechanical strength, heat resistance, and machinability ■ Good sliding properties, usable without lubrication ■ Excellent chemical resistance, does not completely dissolve in acids ■ No rust formation 【Molding modules are also available】 By using "MODULE-4L" to mix the main agent and curing agent, polymerization and curing can be performed within the mold, allowing for direct molding of automotive parts, machine parts, round bars, sheets, pipes, etc., directly from the material. Since silicone molds can be used, production can be achieved at low cost and in a short period. *For more details, please refer to the materials. Feel free to contact us with any inquiries.
Inquire About This Product
basic information
【Various Physical Properties of 3NI-NYLON】*Measured values when dry. (Reference values) ◎3NI Non-reinforced Tensile Strength: 78 MPa Elongation at Break: 13% Flexural Strength: 124 MPa Flexural Modulus: 3320 MPa Izod Impact Value: 45 J/m Deflection Temperature under Load: 177℃ ◎3NI-GF15 (GF Reinforced 15%) Tensile Strength: 96.5 MPa Elongation at Break: 4.4% Flexural Strength: 153 MPa Flexural Modulus: 5100 MPa Izod Impact Value: 34 J/m Deflection Temperature under Load: 211℃ ◎3NI-GF30 (GF Reinforced 30%) Tensile Strength: 111 MPa Elongation at Break: 2.5% Flexural Strength: 175 MPa Flexural Modulus: 6960 MPa Izod Impact Value: 33 J/m Deflection Temperature under Load: 213℃ *For more details, please refer to the materials. Feel free to contact us.
Price range
Delivery Time
Applications/Examples of results
For more details, please refer to the materials. Feel free to contact us as well.
catalog（1）
Download All Catalogs
Company information
Niko Giken Co., Ltd. primarily engages in the manufacturing of various "research and development prototypes" and has built up expertise in producing a wide variety of small quantities of resin products using 3D modeling technology, machining technology, and general casting technology for thermosetting resins since its establishment in 1984. Based on this comprehensive resin processing technology, we have established a unique technology for "casting nylon, specifically nylon 6, which is thermoplastic." Since 2009, we have been developing our nylon casting business centered on technology development, accumulating achievements while responding to customer demands, and received certification as "Composite Nylon Casting Technology" under the "11th Kawasaki Manufacturing Brand." In 2016, to further enhance and systematize the strengths of our unique technology, we established a development headquarters at the "Kawasaki New Industry Creation Center (KBIC)." In 2017, we began brand development under the name "3NI-NYLON." We are collaborating with the "Ikuta PBF Factory," which is equipped with large high-end 3D printers. We are conducting research and development of materials, equipment, and systems to solve QCD challenges required for small-batch production across various fields.
![[Leveling Correction] Leveling correction of concrete floors "Teratec Method"](https://image.mono.ipros.com/public/product/image/d08/1267539002/IPROS70063422645318547243.jpeg?w=280&h=280)