Can you increase the hardness of electroless nickel plating with Silvec?
Q: Is it possible to increase the hardness of electroless nickel plating? A: Yes, it is possible. We perform heat treatment (by the supplier) after our electroless nickel plating to achieve the specified hardness (within the lower and upper limits). The Vickers hardness of our electroless nickel is approximately 550 Hv, and there are products that have been treated to over 900 Hv after heat treatment. While heat treatment may cause discoloration of the electroless nickel plating, it does not affect its functional properties such as hardness. If discoloration is absolutely unacceptable, vacuum heat treatment can prevent discoloration; however, we sincerely apologize that we are unable to accommodate this at our company.
Inquire About This Product
basic information
Silvec's electroless nickel plating primarily involves basket processing. If you have any questions, please feel free to contact us. 【Contact Information】 TEL: 048-994-5931 FAX: 048-994-5935 E-mail: info@silvec.co.jp
Price range
Delivery Time
Applications/Examples of results
catalog（2）
Download All Catalogs
Company information
Silvec Co., Ltd. (Head Office Factory: Yashio City, Saitama Prefecture) has a strong expertise in plating and surface treatment for various aluminum, aluminum die-cast, and zinc die-cast components, and we supply our products to customers nationwide. We are also skilled in precision barrel plating for fine parts. We have a surface treatment factory in Thailand (Chonburi Province) for plating, anodizing, and chemical treatment as our overseas subsidiary. We offer a one-stop service from material procurement to surface treatment through our extensive network. If you have any inquiries regarding surface treatment for metals, we can provide some suggestions. Please feel free to contact us.
![[Data] EMC Testing for In-Vehicle Equipment - Basic Standards Required by Various Automobile Manufacturers](https://image.mono.ipros.com/public/product/image/20d/2000478812/IPROS34405117686661351179.jpeg?w=280&h=280)