The standard master batch of CR can be purchased starting from 21 kg!!
TB3510LC is a masterbatch with a hardness of 50 degrees that meets the recent demand for smaller quantities of chloroprene rubber, while also possessing physical properties such as a tensile strength of over 10 MPa and low specific gravity. It is a rubber compound weighing 21 kg, which includes 1 kg of curing agent batch attached to 20 kg of A-mixed rubber. By mixing these components, CR final rubber (hardness 50 degrees) can be produced. For example, if 5 kg of rubber material is needed, 250 g of curing agent batch should be used and mixed in. For users who do not have rubber mixing rolls, we can perform the final processing and send it out (additional processing fees apply). We also offer standard batches with hardness ranging from 40 to 80 degrees. Please check the product description section for various physical properties!
Inquire About This Product
basic information
The properties of TB3510LC are as follows: ● Normal properties - Hardness (JIS-A): 52 - Specific gravity of vulcanizate: 1.32 - Compound ML (1+4) at 100°C: 28 - Tensile strength (MPa): 14.3 - Elongation (%): 455 ● Heat resistance (100°C × 70 hours) - Hardness change (%): +10 - Tensile change (%): +4 - Elongation change (%): -23 ● Oil resistance (100°C × 70 hours) - IRM901 (equivalent to No. 1 oil) volume change rate (%): +3.0 ● Compression set - 70°C × 22 hours (%): 22 ● Ozone resistance (50 ppm, 40°C, 20%, 70 hours): No cracks ● Type of polymer: General grade *The above properties are measured values and do not guarantee the product.
Price information
@600/kg (1 bag 12,600 yen) Shipping and consumption tax will be charged separately at actual cost.
Price range
P2
Delivery Time
P2
※The first time may take some time.
Applications/Examples of results
It can be used for various rubber products such as rubber packing and rubber bushes!!